Feature size reduction of silicon slot waveguides by partial filling using atomic layer deposition

[+] Author Affiliations
Tapani Alasaarela, Antti Säynätjoki, Teppo Hakkarainen, Seppo Honkanen

Helsinki University of Technology, Department of Micro and Nanosciences, Tietotie 3, Espoo 02015, Finland

Opt. Eng. 48(8), 080502 (August 17, 2009). doi:10.1117/1.3206731
History: Received April 28, 2009; Revised July 03, 2009; Accepted July 07, 2009; Published August 17, 2009
Text Size: A A A

Open Access Open Access

We propose a novel method to realize silicon-on-insulator (SOI)–based air slot waveguides for sensing applications. The method, based on feature size reduction using conformal thin films grown by atomic layer deposition (ALD), enables a guided slot mode in a silicon slot waveguide with a patterned slot width of more than 200nm. Feature size reduction of slot structures with ALD grown amorphous TiO2 is demonstrated.

Figures in this Article

Slot waveguides are high-index contrast waveguide structures where light is confined in a slot with low-index material or air.12 The ability to guide light in lower index materials offers a way to make new kinds of active and passive waveguide structures on the well-established silicon platform by the integration of materials that are known from glass and polymer waveguides. Filling of slot waveguides with highly nonlinear organic materials3 and electro-optical polymers4 has been demonstrated, but successful filling of slots, particularly with inorganic materials, has turned out to be difficult.

Typical vertical slot waveguides for 1.55-μm wavelength have a rail width in the 200-nm and slot width in 100-nm regime. The small feature size makes the fabrication of vertical slot waveguides difficult. The 193-nm-deep UV (DUV) lithography or electron-beam lithography processes can be used, but as the feature size is not far from the minimum achievable, reproducible fabrication becomes a challenging task. The minimum feature size can be increased by reducing the index contrast with, e.g., the silicon nitride/silicon oxide platform5 or by the complete filling of the air slot in silicon-on-insulator (SOI). However, it is the index contrast that gives rise to the slot mode, and reducing the contrast therefore weakens the slot mode character of the mode. Moreover, in sensing applications, the measured gas or liquid should interact with the air slot for maximum sensitivity. Silicon slot waveguides have already been demonstrated as gas detectors.6

Atomic layer deposition (ALD) was developed for making thin film electroluminescent (TFEL) displays.7 Since then, it has been utilized in many different applications and has become a standard CMOS process in the semiconductor industry. ALD is a pulsed modification of chemical vapor deposition technology. It is based on successive, surface-controlled reactions from the gas phase. As the reactions happen only at the surface, the process is self-limiting, the growth rate is well controlled, and the grown films are extremely conformal over the surfaces.

Due to its low growth rate, ALD is usually considered feasible only for very thin films, but the low growth rate can be compensated with the easily increased batch size. Therefore, TFEL displays with more than micron thick atomic layer deposited high-quality ZnS:Mn phosphors and Al-Ti-oxide (ATO) dielectrics are in large-scale production.

We propose a novel way to realize air slot waveguides on an SOI platform using atomic layer deposited high refractive index thin films. We show that a conformal film of a high refractive index material grown onto the structure can enable the slot modes on SOI slot waveguides with a slot width of 200nm. A good example of such film is the amorphous TiO2 grown by low-temperature ALD.

In order to study the feasibility of the proposed method, the properties of the slot waveguide pictured in Fig. 1 are simulated by using the film mode matching (FMM) solver of the FIMMWAVE software.8 The rail width used is 180nm, rail height is 220nm, and slot width is 200nm. The thickness d of the ALD material is varied between 40nm and 100nm. For the simulations, we use a wavelength of 1.55μm. As the refractive index of the ALD material, we use 2.2 (amorphous TiO2). When d is below 40nm, the waveguide has no guided slot mode, and above 100nm, the slot is completely filled.

Graphic Jump LocationF1 :

The proposed slot waveguide structure.

The effective indices of the quasi–transverse electric (TE) modes are shown in Fig. 2. With d>90nm, a second-order quasi-TE mode is found for the waveguide. The second-order mode is asymmetric and does not have field confinement in the air slot. The rail height can be made smaller to eliminate the second-order mode [and also the quasi–transverse magnetic (TM) mode] and to realize a slot waveguide with only a single quasi-TE slot mode.

Graphic Jump LocationF2 :

The effective indices for the simulated slot waveguide structures as a function of the ALD film thickness d.

The transverse electric field profiles for the cases with d=60, 70, and 80nm are shown in Fig. 3. The mode field profiles show that the modes in these partially filled structures are well confined in the air slot.

Graphic Jump LocationF3 :

The quasi-TE mode field profiles and their cross sections at the middle of the slot for the slot waveguides with ALD film thickness of (a) d=60nm, (b) d=70nm, and (c) d=80nm.

To demonstrate the filling of slots with ALD, we did experiments with test slot structures of different widths using standard silicon wafers. The result of a filling experiment with 100nm of amorphous TiO2 grown at a low temperature is shown in Fig. 4. The structures have nonstraight sidewalls and rounded corners, which are due to the natural features of the etching processes and the ALD growth. The deposition was done using Beneq TFS-500 ALD reactor using TiCl4 and water as precursors. The process used for TiO2 is well known and produces good quality films. A relatively low growth temperature of 120°C was chosen to get amorphous films, which are expected to yield minimal scattering losses in waveguides.

Graphic Jump LocationF4 :

Scanning electron micrograph (SEM) of slots fabricated to a (100) silicon wafer and an ALD coated with 100nm of amorphous TiO2 using TiCl4 and water in 120°C. The leftmost slot structure resembles the one simulated in Fig. 3.

To confirm the good waveguiding properties of the ALD-grown amorphous TiO2 films, we deposited approximately 460-nm-thick films on glass substrates using similar processing parameters as in slot filling experiments. The properties of these slab waveguides were measured using the well-known prism coupling technique with a Metricon 2010/M Prism Coupler having the loss measurement feature as an option. As expected, at 1.55-μm wavelength, the slabs guided one TE-mode with a measured effective index of 2.03, which gives a refractive index of about 2.25 for the films. The propagation losses were estimated by scanning a multimode optical fiber along the light propagation direction and measuring the scattered light. The measured propagation losses are <1dBcm, which is close to the measurement accuracy of the technique. The loss of 1dBcm should not be significant in slot waveguides, where losses of 10dBcm or 15dBcm have been measured.3,9

The ALD technology opens many new possibilities for realizing new kinds of slot waveguide structures. The digital atomic layer accurate control of thickness on all surfaces enables the design of easily realizable sandwich structures on vertical as well as horizontal surfaces. Also, a wide range of materials can be deposited for different purposes.10

In this letter, we have discussed the possibility of realizing slot waveguides with wide silicon slots and ALD-grown amorphous TiO2 thin films. The simulations show that a silicon slot waveguide covered with a high refractive index material has good electric field confinement in the remaining air slot. The initial processing and ALD growth trials show that a conformal film of amorphous TiO2 can be easily grown into slot structures. ALD also has a natural surface smoothing feature, which should reduce the waveguide scattering losses.

Acknowledgments

Petri Stenberg and Markku Kuittinen of the University of Joensuu are gratefully acknowledged for providing the slot structures for the demonstration. Jussi Hiltunen of VTT Technical Research Centre of Finland is acknowledged for the prism coupling measurements, and Ville Malinen of Beneq Oy for providing the TiO2 slab waveguide samples. This work was supported by the Academy of Finland and Tekes. T.A. also acknowledges support from the Graduate School of Modern Optics and Photonics, Walter Ahlström Foundation, and The Finnish Foundation for Economic and Technology Sciences—KAUTE.

Almeida  V. R., , Xu  Q., , Barrios  C. A., , and Lipson  M., “ Guiding and confining light in void nanostructure. ,” Opt. Lett..  0146-9592 29, (11 ), 1209–1211  ((2004)).
Xu  Q., , Almeida  V. R., , Panepucci  R. R., , and Lipson  M., “ Experimental demonstration of guiding and confining light in nanometer-size low-refractive-index material. ,” Opt. Lett..  0146-9592 29, (14 ), 1626–1628  ((2004)).
Koos  C., , Vorreau  P., , Vallaitis  T., , Dumon  P., , Bogaerts  W., , Baets  R., , Esembeson  B., , Biaggio  I., , Michinobu  T., , Diederich  F., , Freude  W., , and Leuthold  J., “ All-optical high-speed signal processing with silicon-organic hybrid slot waveguides. ,” Nature Photon..  1749-4885 3, (4 ), 216—219  ((2009)).
Hochberg  M., , Baehr-Jones  T., , Wang  G., , Huang  J., , Sullivan  P., , Dalton  L., , and Scherer  A., “ Towards a millivolt optical modulator with nano-slot waveguides. ,” Opt. Express.  1094-4087 15, (13 ), 8401–8410  ((2007)).
Barrios  C. A., , Sánchez  B., , Gylfason  K. B., , Griol  A., , Sohlström  H., , Holgado  M., , and Casquel  R., “ Demonstration of slot-waveguide structures on silicon nitride / silicon oxide platform. ,” Opt. Express.  1094-4087 15, (11 ), 6846–6856  ((2007)).
Robinson  J. T., , Chen  L., , and Lipson  M., “ On-chip gas detection in silicon optical microcavities. ,” Opt. Express.  1094-4087 16, (6 ), 4296–4301  ((2008)).
Suntola  T., and Antson  J., “ Method for producing compound thin films. ,” U.S. Patent No. 4,058,430 ((1977)).
FIMMWAVE 5.1,  Photon Design Ltd , www.photond.com ((2008)).
Baehr-Jones  T., , Hochberg  M., , Walker  C., , and Scherer  A., “ High-Q optical resonators in silicon-on-insulator based slot waveguides. ,” Appl. Phys. Lett..  0003-6951 86, , 081101  ((2005)).
Puurunen  R. L., “ Surface chemistry of atomic layer deposition: A case study for the trimethylaluminum/water process. ,” J. Appl. Phys..  0021-8979 97, , 121301  ((2005)).
© 2009 Society of Photo-Optical Instrumentation Engineers

Citation

Tapani Alasaarela ; Antti Säynätjoki ; Teppo Hakkarainen and Seppo Honkanen
"Feature size reduction of silicon slot waveguides by partial filling using atomic layer deposition", Opt. Eng. 48(8), 080502 (August 17, 2009). ; http://dx.doi.org/10.1117/1.3206731


Figures

Graphic Jump LocationF1 :

The proposed slot waveguide structure.

Graphic Jump LocationF2 :

The effective indices for the simulated slot waveguide structures as a function of the ALD film thickness d.

Graphic Jump LocationF3 :

The quasi-TE mode field profiles and their cross sections at the middle of the slot for the slot waveguides with ALD film thickness of (a) d=60nm, (b) d=70nm, and (c) d=80nm.

Graphic Jump LocationF4 :

Scanning electron micrograph (SEM) of slots fabricated to a (100) silicon wafer and an ALD coated with 100nm of amorphous TiO2 using TiCl4 and water in 120°C. The leftmost slot structure resembles the one simulated in Fig. 3.

Tables

References

Almeida  V. R., , Xu  Q., , Barrios  C. A., , and Lipson  M., “ Guiding and confining light in void nanostructure. ,” Opt. Lett..  0146-9592 29, (11 ), 1209–1211  ((2004)).
Xu  Q., , Almeida  V. R., , Panepucci  R. R., , and Lipson  M., “ Experimental demonstration of guiding and confining light in nanometer-size low-refractive-index material. ,” Opt. Lett..  0146-9592 29, (14 ), 1626–1628  ((2004)).
Koos  C., , Vorreau  P., , Vallaitis  T., , Dumon  P., , Bogaerts  W., , Baets  R., , Esembeson  B., , Biaggio  I., , Michinobu  T., , Diederich  F., , Freude  W., , and Leuthold  J., “ All-optical high-speed signal processing with silicon-organic hybrid slot waveguides. ,” Nature Photon..  1749-4885 3, (4 ), 216—219  ((2009)).
Hochberg  M., , Baehr-Jones  T., , Wang  G., , Huang  J., , Sullivan  P., , Dalton  L., , and Scherer  A., “ Towards a millivolt optical modulator with nano-slot waveguides. ,” Opt. Express.  1094-4087 15, (13 ), 8401–8410  ((2007)).
Barrios  C. A., , Sánchez  B., , Gylfason  K. B., , Griol  A., , Sohlström  H., , Holgado  M., , and Casquel  R., “ Demonstration of slot-waveguide structures on silicon nitride / silicon oxide platform. ,” Opt. Express.  1094-4087 15, (11 ), 6846–6856  ((2007)).
Robinson  J. T., , Chen  L., , and Lipson  M., “ On-chip gas detection in silicon optical microcavities. ,” Opt. Express.  1094-4087 16, (6 ), 4296–4301  ((2008)).
Suntola  T., and Antson  J., “ Method for producing compound thin films. ,” U.S. Patent No. 4,058,430 ((1977)).
FIMMWAVE 5.1,  Photon Design Ltd , www.photond.com ((2008)).
Baehr-Jones  T., , Hochberg  M., , Walker  C., , and Scherer  A., “ High-Q optical resonators in silicon-on-insulator based slot waveguides. ,” Appl. Phys. Lett..  0003-6951 86, , 081101  ((2005)).
Puurunen  R. L., “ Surface chemistry of atomic layer deposition: A case study for the trimethylaluminum/water process. ,” J. Appl. Phys..  0021-8979 97, , 121301  ((2005)).

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging & repositioning the boxes below.

Related Book Chapters

Topic Collections

PubMed Articles
Advertisement
  • Don't have an account?
  • Subscribe to the SPIE Digital Library
  • Create a FREE account to sign up for Digital Library content alerts and gain access to institutional subscriptions remotely.
Access This Article
Sign in or Create a personal account to Buy this article ($20 for members, $25 for non-members).
Access This Proceeding
Sign in or Create a personal account to Buy this article ($15 for members, $18 for non-members).
Access This Chapter

Access to SPIE eBooks is limited to subscribing institutions and is not available as part of a personal subscription. Print or electronic versions of individual SPIE books may be purchased via SPIE.org.