Characteristic strength and Weibull modulus of selected infrared-transmitting materials

Claude A. Klein; Richard P. Miller; Richard L. Gentilman

doi:10.1117/1.1517578

1 December 2002 Characteristics strength and Weibull modulus of selected infrared-transmitting materials

Claude A. Klein, Richard P. Miller, Richard L. Gentilman

Optical Engineering, Vol. 41, Issue 12, (December 2002). https://doi.org/10.1117/1.1517578

The results of fracture testing are usually reported in terms of a measured strength σ_M = sigma;i∓&Deltaσi where σi is the average of the recorded peak stresses at failure, and ;&Deltaσi represents the standard deviation. This "strength" does not provide an objective measure of the intrinsic strength since σ_M depends on the test method and the size of the volume or the surface subjected to tensile stresses. We first clarify issues relating to the application of Weibull's theory of brittle fracture and then make use of the theory to assess the results of equibiaxial flexure testing carried out on selected IR-transmitting materials. Since equibiaxial flexure testing has now been adopted as the preferred method for measuring the strength of optical materials, we describe the failure-probability distribution in terms of a characteristic strength σ_C—i.e., the effective strength of a uniformly stressed 1-cm² area—which enables us to predict the average stress at failure in a concentric ring configuration if the Weibull modulus m is available. A Weibull statistical analysis of flexural strength data thus amounts to obtaining the parameters σ_C and m, which is best done by directly fitting estimated cumulative failure probabilies to the appropriate failure-probability expression derived from Weibull's theory. Ring-on-ring fracture testing performed at four mechanical test facilities on five lots of Raytran^TM materials [AlON, chemically vapor deposited (CVD) diamond, ZnSe, standard ZnS, and multispectral ZnS], on sapphire specimens cut in the a-, the c-, and the r-plane orientations, and on Oxyfluoride^TM glass validates the procedure and demonstrates that, in many instances, the wide divergence of measured strengths can be attributed to the size of the stressed area.

©(2002) Society of Photo-Optical Instrumentation Engineers (SPIE)

Citation Download Citation

Claude A. Klein, Richard P. Miller, and Richard L. Gentilman "Characteristics strength and Weibull modulus of selected infrared-transmitting materials," Optical Engineering 41(12), (1 December 2002). https://doi.org/10.1117/1.1517578

Published: 1 December 2002

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available