Interfacial shear strength estimates of NiTi-Al matrix composites fabricated via ultrasonic additive manufacturing

Adam Hehr; Joshua Pritchard; Marcelo J. Dapino

doi:10.1117/12.2046317

10 March 2014 Interfacial shear strength estimates of NiTi-Al matrix composites fabricated via ultrasonic additive manufacturing

Adam Hehr, Joshua Pritchard, Marcelo J. Dapino

Author Affiliations +

Proceedings Volume 9059, Industrial and Commercial Applications of Smart Structures Technologies 2014; 905906 (2014) https://doi.org/10.1117/12.2046317
Event: SPIE Smart Structures and Materials + Nondestructive Evaluation and Health Monitoring, 2014, San Diego, California, United States

Abstract

The purpose of this study is to understand and improve the interfacial shear strength of metal matrix composites fabricated via very high power (VHP) ultrasonic additive manufacturing (UAM). VHP-UAM NiTi-Al composites have shown a dramatic decrease in thermal expansion compared to Al, yet thermal blocking stresses developed during thermal cycling have been found to degrade and eventually cause interface failure. Consequently, to improve understanding of the interface and guide the development of stronger NiTi- Al composites, the interface strength was investigated through the use of single ber pullout tests. It was found that the matrix yielded prior to the interface breaking since adhered aluminum was consistently observed on all pullout samples. Additionally, measured pullout loads were utilized as an input to a nite element model for stress and shear lag analysis, which, in turn showed that the Al matrix experienced a peak shear stress near 230 MPa. This stress is above the Al matrix's ultimate shear strength of 150-200 MPa, thus this large stress corroborates with matrix failure observed during testing. The in uence of various ber surface treatments on bond mechanisms was also studied with scanning electron microscopy and energy dispersive X-ray spectroscopy.

Citation Download Citation

Adam Hehr, Joshua Pritchard, and Marcelo J. Dapino "Interfacial shear strength estimates of NiTi-Al matrix composites fabricated via ultrasonic additive manufacturing", Proc. SPIE 9059, Industrial and Commercial Applications of Smart Structures Technologies 2014, 905906 (10 March 2014); https://doi.org/10.1117/12.2046317

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available