Quantum dots (QDs) have extraordinary strong light absorption and size tunable bandgap. However, QD films are typically limited to ~200-300 nm due to their poor charge mobility. This severely limits the quantum efficiency of QD devices for λ <750 nm (infrared). Herein, we report a record 1 μm thick QD film using intercalated graphene layers as transparent current extractors. This overcomes QD poor mobility, ensuring both effective light absorption and charge extraction towards the near-infrared reaching quantum efficiency (EQE) of 90%.
The short diffusion length (LD<200 nm) of QDs limits their useful thickness to ~200-300 nm1–4 , resulting in poor infrared light absorption. To overcome this limitation, we have built a 1 µm thick QD film with intercalated transparent graphene electrodes that keep high charge collection efficiency. As a result, the 1 µm intercalated devices show a superior EQE reaching 90% at λ ~800 nm without the drop of quantum efficiency at λ ~700 nm observed in most QD devices. The EQE of intercalated devices improves over the entire λ~ 600-1100 nm spectrum as the thickness increases from 100 nm to 1 μm, clearly breaking the restriction that the diffusion length of QDs imposes on the film thickness. This improves absorption and charge collection in the infrared.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.